Investment Materials

Dental investment materials are used to encase the wax designed for the lost wax casting technique. These materials are usually available as a powder that is mixed with water and then used to encase the wax design. These materials solidify and can withstand the heat of the casting furnace to hold the precise shape left behind when the wax is burned out. Different gypsums are designed for use with different dental alloys or other materials, so be sure to select the proper gypsum for the case at hand.
CompanyWhip Mix CorporationWhip Mix CorporationWhip Mix CorporationWhip Mix CorporationWhip Mix Corporation
ItemResinVestBeauty-Cast Gypsum InvestmentFastFire 15 Phosphate InvestmentNovocast Investment MaterialSoldering Investment
PriceInquireInquireInquireInquireInquire
DescriptionDesigned for burning out printed or milled resin patterns for crowns, bridges, or frameworks, ResinVest is a fiber-reinforced material that resists The proven standard for the Hygroscopic Technique. Also excellent for the High Heat Technique.FASTFIRE 15 is a fine grain phosphate investment which requires only a 15 minute benchset before placing molds into a hot oven for rapid burnout. It NOVOCAST is an advanced inlay investment that provides increased accuracy for casting conventional gold alloys at a mold temperature of 650 degrees C Multi-purpose SOLDERING INVESTMENT isideal for soldering all types of dental alloys, including chrome-cobalt. Its fine texture mixes readily with
Quantity100 g Package; 55 lbs. Carton144 - 75 g Package
144 - 50 g Package
24 - 50 g Package
11 kg (25 pounds) Carton		100 - 90 g Package
150 - 60 g Package
25 - 90 g Package
25 - 60 g Package
340 mL Bottle
1 L Bottle
6 Pack - 340 mL Bottles
6 Pack - 1 L Bottles
9 kg (2 pounds) Carton		9 kg (20 pounds) Carton
24 - 50 g Package
24 - 75 g Package
144 - 50 g Package
144 - 75 g Package		2 kg (4.5 pounds) Package
11 kg (25 pounds) Carton
Compressive Strength1,350 psi (9.2 MPa)Wet - 700 psi (5 MPa)Wet - 500 psi (3.4 MPa)Wet - 950 psi (7 MPa)Wet - 1,200 psi (9 MPa)
Working Time6 to 8 Minutes3 minutes7 - 9 minutes3 minutes2 - 3 minutes
Set Time30 Minutes Minimum14.5 minutesNot Available15 minutes15 minutes
Material TypePhosphate InvestmentGypsum Casting InvestmentFine Grain PhosphateGypsum Bonded InvestmentGypsum Bonded Investment
Indication For UseBurning out milled or printed resin patternsLow Fusing Crown and Bridge AlloysUniversal Phosphate Investment for All Crown and Bridge AlloysLow Fusing Crown and Bridge AlloysLow and High Fusing Precious Metals
Liquid / Powder Ratio22 ml/100 g30 mL/100 g27 mL / 100 g34 mL / 100 g24 mL / 100 g
Setting Expansion1.6 Percent0.4 %1 %0.45 %0.25 %
Ready For BurnoutYes30 minutes15 minutes30 minutes30 Minutes
Hygroscopic ExpansionNot Available1.5 %N / AN / AN / A
Thermal Expansion0.65 Percent480º C (900º F) - 0.55%
650º C (1,200º F) - 1.20%		1.0 %650° C - 1.20 %700° C (1,300° F) - 0.60 %
Metal or Ringless TechniqueBothMetal OnlyMetal or RinglessMetal OnlyN / A
Get InfoNot AvailableNot AvailableNot AvailableNot AvailableNot Available