Dental alloys are used for a casting a range of restorations, copings, frames and more. These alloys can be composed of a range of noble, high noble and base metals, and each mixture offers different properties that can make one alloy ideal for a specific restorative situation and another alloy completely unsuited to the same task. Full contour crowns and bridges are most often case from noble and high noble metals such as gold and platinum, but these softer metals might not be suited for posterior crowns on a bruxing patient. A wider range of alloys can be used for casting copings and substructures for porcelain-fused-to-metal (PFM) restorations. It is important to coordinate the alloy and the ceramic systems being used for a PFM restoration. Casting dental alloys requires specific techniques with different alloys melting at different temperatures, so be sure to follow the protocols that deliver the best results for your lab.
| | | | | |
Company | Dentsply Sirona Prosthetics | Dentsply Sirona Prosthetics | Dentsply Sirona Prosthetics | Dentsply Sirona Prosthetics | Dentsply Sirona Prosthetics |
Item | Majority Crown and Bridge Alloy | Degudent LS Porcelain Alloy | Image 2 Porcelain Alloy | Ney-Oro PF-CB Crown and Bridge Alloy | Palliag M Crown and Bridge Alloy |
Price | Inquire | Inquire | Inquire | Inquire | Inquire |
Description | Type III. Flexibility is Majority's premier asset. Soften to Type II ductility levels for onlays or harden to Type IV strength for high stress | Degudent LS is a micro-fine, extra-hard alloy suitable for MOD's, single crowns, long span bridgework, milled restorations in conjunction with | Type IV micro-fine grain alloy that is recommended for single crowns, long span bridges and implant superstructures. Low fusing benefits. | Type III. Palladium-free for outstanding gold color with excellent tarnish resistance. PF-CB is a great multi- purpose alloy due to its combination of | Palliag M is a Type IV, noble, platinum colored Crown & Bridge Alloy containing 2%; gold. This economical, versatile alloy can be used for all crown |
Composition | Gold: 50 %
Palladium: 4.5 %
Silver: 10 %
Copper: 31 %
Zinc: Less Than 1 %
Iridium: Less Than 1 % | Gold: 73.1 %
Platinum: 1.5 %
Palladium: 5.8 %
Silver: 16 %
Tin: Less Than 1 %
Zince: Less Than 1 %
Iridium: Less Than 1 % | Gold: 84.5 %
Platinum: 6.9 %
Palladium: 5 %
Silver: 1 %
Zinc: Less Than 1 %
Indium: Less Than 1 %
Iron: Less Than 1 %
Rhenium: Less Than 1 %
| Gold: 80 %
Platinum: 1 %
Silver: 9%
Copper: 9 %
Zinc: Less Than 1 %
Iridium: Less Than 1 % | Gold: 2 %
Palladium: 27.4 %
Silver: 58.5 %
Copper: 10.5 %
Zinc: Less Than 1 %
Iridium: Less Than 1 % |
Hardness | 220 HV | 235 HV | 230 HV | 126 HV | 310 HV |
Tensile Strength | 526 N/mm2 | 560 N/mm2 | 671 N/mm2 | 275 N/mm2 | 940 N/mm2 |
Indications for Use | Not Available | MOD's
Single Crowns
Long Span Bridgework
Milled Restorations In Conjunction
With Precision Attachments
Partial Dentures
Implant Superstructures | Single Crowns
Long Span Bridges
Implant Superstructures | Inlays Single Crowns Partial Dentures Long Span Bridgework Milled Restorations | Crown Types Including
Milled Telescopic Crowns
Connectors And Attachments
Long Span Bridges
Cast Partial Dentures |
Color | Gold | Gold | Gold | Gold | White |
Compatible Porcelains | Not Available | Duceragold Porcelain | Duceragold Porcelain | Not Available | Not Available |
Melting Interval | 835° C - 885° C | 985° C - 1,065° C | 1,090° C - 1,195° C | 885° C - 935° C | 950° C - 1,040° C |
Casting Temperature | 990° C | 1,200° C | 1,290° C | 1,025° C | 1,200° C |
Expansion | 7 % | 5 % | 7 % | 45 % | 3 % |
Get Info | Not Available | Not Available | Not Available | Not Available | Not Available |