Dental alloys are used for a casting a range of restorations, copings, frames and more. These alloys can be composed of a range of noble, high noble and base metals, and each mixture offers different properties that can make one alloy ideal for a specific restorative situation and another alloy completely unsuited to the same task. Full contour crowns and bridges are most often case from noble and high noble metals such as gold and platinum, but these softer metals might not be suited for posterior crowns on a bruxing patient. A wider range of alloys can be used for casting copings and substructures for porcelain-fused-to-metal (PFM) restorations. It is important to coordinate the alloy and the ceramic systems being used for a PFM restoration. Casting dental alloys requires specific techniques with different alloys melting at different temperatures, so be sure to follow the protocols that deliver the best results for your lab.
|  |  |  |  |  |
| Company | Argen | Argen | Argen | Argen | Argen |
| Item | ARGELITE 71 Porcelain Alloy | ARGEDENT EURO Porcelain Alloy | Argenco 75 Crown and Bridge Alloy | Captek Nano Crown and Bridge Material | NOBLECROWN NF Porcelain Alloy |
| Price | Inquire | Inquire | Inquire | Inquire | Inquire |
| Description | Argelite 71 gives a high strength alloy that can be used to both processing and layering porcelains. The low silver content and light oxide give | Argedent EURO is a versatile High Noble alloy that casts, finishes, solders and laser welds very easily, with broad porcelain compatibility. Argedent | Type III - Hard crown and bridge alloy. | Captek Nano Crowns and Bridges offer the esthetics of metal-free restorations with the predictability, versatility and strength of traditional metal | NobleCrown NF is an economical, white color, Noble porcelain alloy formulated to be compatible with all major porcelains. Superior physical properties |
| Composition | Palladium: 70.9 %
Silver: 10 %
Indium: 8 %
Tin: 5.3 %
Zinc: 5 %
Ruthenium: Less Than 1 %
Gallium: Less Than 1 % | Gold: 40 %
Palladium: 39.4 %
Silver: 10 %
Indium: 8.8 %
Gallium: 1.4 %
Ruthenium: Less Than 1 %
Tin: Less Than 1 %
| Gold: 74.5 %
Palladium: 3.5 %
Silver: 11 %
Copper: 10.45 %
Zinc: Less Than 1 %
Iridium: Less Than 1 % | Gold: 84 %
Palladium: 7.2 %
Platinum: 5.3 % | Cobalt: 42.75 %
Palladium: 25 %
Chromium: 20 %
Molybdenum: 12 %
Boron: Less Than 1 % |
| Hardness | After Firing: 300 HV | Soft: 260 HV
Hard: 290 HV | 182 HV | Not Available | After Firing: 335 HV |
| Tensile Strength | Soft: 830 N/mm2
Hard: --- | Soft: 800 N/mm2
Hard: 840 N/mm2 | Not Available | Not Available | Soft:690 N/mm2
Hard: --- |
| Indications for Use | Not Available | Single Crown
Multi-Units & Bridges | Crowns
Bridges | Crowns (Anterior and Posterior)
Bridgework Up To 8
Implant Crowns And Bridges | Single Crown
Multi-Units & Bridges |
| Color | White | White | Yellow | Yellow Gold | White |
| Compatible Porcelains | Not Available | Not Available | Not Available | Not Available | All Major Porcelains |
| Melting Interval | 1,185º C - 1,285º C | 1,120º C - 1,260º C | 932° C - 960° C | Not Available | 1,250º C - 1,290º C |
| Casting Temperature | 1,340º C | 1,400º C | 1,037° C | Not Available | 1,400º C |
| Expansion | 14.2 µm/mm-° C At 500º C | 14.1 µm/mm-º C At 500º C | Not Available | Not Available | 14.4 µm/mm-º C At 500º C |
| Get Info | Not Available | Not Available | Not Available | Not Available | Not Available |