Dental Solder

Dental solder can be used for orthodontics as well as restorative cases. These small metal wires are heated and melted to connect other metal restoration parts or to repair cast metal frameworks. When purchasing dental solder, be sure to note the high end melting range and ensure it is below the low end melting range of the metal you are soldering to.
CompanySterngold Dental, LLCSterngold Dental, LLCSterngold Dental, LLCSterngold Dental, LLCSterngold Dental, LLC
ItemStern Electrosolder585 Fine Yellow Post-Solder615 Fine Yellow Post-SolderChrome 2 White Post-SolderMF-Y
PriceInquireInquireInquireInquireInquire
Quantity2 dwt Strip1 dwt Strips1 dwt Strips1 dwt Strips1 dwt Strip
Material TypeLaminated Strip Solder Onto One Side
Pure Gold On Other Side		Gold
Silver		Gold
Silver		Platinum-Gold-Palladium Wire Clasps to Cobalt-ChromiumGold
Silver
Indication For UseElectrosolderingNot AvailableNot AvailableAny Type of Crown and Bridge SolderingPre-Solder Investment Material For Yellow Ceramic
ColorNot AvailableYellowYellowWhiteYellow
% Au59.558.561.558.3050
% Ag24.516.914.917.1537.5
Melting Range700 to 760°C738 to 793°C763 to 801°C657 to 704°C1104 to 1132°C
%Pd1.0Not AvailableNot AvailableNot Available11
% Zn15Not AvailableNot AvailableNot AvailableNot Available
DescriptionSpecifically developed for electrosoldering, each laminated strip has solder on one side and pure gold on the other. The thickness of 2 Dwt strip and Whenever possible, select a solder with a high end melting range value at least 100°F (40°C) below the low end of your alloy's melting range. All our Whenever possible, select a solder with a high end melting range value at least 100°F (40°C) below the low end of your alloy's melting range. All our Chrome 2 is a popular regular solder. Originally developed for connecting platinum-gold-palladium wire clasps to cobalt-chromium removable partial Yellow Presolder. It flows magnificently and bonds beautifully to both noble and base metals. In fact, unless you need a white solder or want a
Get InfoInquireInquireInquireInquireInquire
-->