Dental investment materials are used to encase the wax designed for the lost wax casting technique. These materials are usually available as a powder that is mixed with water and then used to encase the wax design. These materials solidify and can withstand the heat of the casting furnace to hold the precise shape left behind when the wax is burned out. Different gypsums are designed for use with different dental alloys or other materials, so be sure to select the proper gypsum for the case at hand.
| | | | | |
Company | Whip Mix Corporation | Whip Mix Corporation | Whip Mix Corporation | Whip Mix Corporation | Whip Mix Corporation |
Item | PC 15 Phosphate Bonded Investment | Ceramigold Investment with Carbon | Novocast Investment Material | ResinVest | X-20 Chrome Phosphate Investment |
Price | Inquire | Inquire | Inquire | Inquire | Inquire |
Description | PC15 is a fine grained phosphate bonded investment for pressable ceramics. Its creamy consistency pours easily when investing and produces smooth | This phosphate investment contains carbon for bright, gold-colored castings. Expansion can be controlled to fit your needs -- yet technic is easy to | NOVOCAST is an advanced inlay investment that provides increased accuracy for casting conventional gold alloys at a mold temperature of 650 degrees C | Designed for burning out printed or milled resin patterns for crowns, bridges, or frameworks, ResinVest is a fiber-reinforced material that resists | A vastly improved casting investment for making chrome partial denture frameworks. For casting any chrome partial alloy. Refractory Cast is hard, |
Quantity | 25 - 100 g Package 100 - 100 g Package 6 Pack - 340 mL Bottles 6 Pack - 1 L Bottles 340 mL Bottle 1 L Bottle | 144 - 90 g Package 144 - 60 g Package 6 Pack - 340 mL Bottles 6 Pack - 1 L Bottles 340 mL Bottle 1 L Bottle | 9 kg (20 pounds) Carton 24 - 50 g Package 24 - 75 g Package 144 - 50 g Package 144 - 75 g Package | 100 g Package; 55 lbs. Carton | 22 kg (50 pounds) Carton 50 - 400 g Packages 25 kg (55 pounds) Carton 6 Pack - 340 mL Bottles 6 Pack - 1 L Bottles 340 mL Bottle 1 L Bottle |
Compressive Strength | Wet - 500 psi (3.4 MPa) | Wet - 1,500 psi (10 MPa) | Wet - 950 psi (7 MPa) | 1,350 psi (9.2 MPa) | Wet - 2,500 psi (17 MPa) |
Working Time | 7 - 9 minutes | 6 - 7 minutes | 3 minutes | 6 to 8 Minutes | 4 - 5 minutes |
Set Time | Not Available | Not Available | 15 minutes | 30 Minutes Minimum | Not Available |
Material Type | Fine Grain Phosphate Bonded Investment | Phosphate Bonded Investment | Gypsum Bonded Investment | Phosphate Investment | Phosphate Bonded |
Indication For Use | Pressable Ceramics | Crown and Bridge and Ceramic Gold Alloys | Low Fusing Crown and Bridge Alloys | Burning out milled or printed resin patterns | Casting Partials with Chromium Dental Alloys |
Liquid / Powder Ratio | 27 mL / 100 g | 16 mL /100 g | 34 mL / 100 g | 22 ml/100 g | 11 mL / 100 g |
Setting Expansion | 1 % | 0.7 % | 0.45 % | 1.6 Percent | 0.2 % |
Ready For Burnout | 15 minutes | 60 minutes | 30 minutes | Yes | 30 - 60 minutes |
Hygroscopic Expansion | N / A | N / A | N / A | Not Available | N / A |
Thermal Expansion | 0.7 % | 1.2 % | 650° C - 1.20 % | 0.65 Percent | 700 -- 1,000° C (1,300 -- 1,800° F) - 0.90 % |
Metal or Ringless Technique | Metal or Ringless | Metal or Ringless | Metal Only | Both | Metal or Ringless |
Get Info | Not Available | Not Available | Not Available | Not Available | Not Available |